AWS/ASME A 5.8 B Ag-20
| FEATURES & APPLICATIONS |
Low temperature joining of dissimilar metals. Excellent where tolerances and fit are not perfect.
- Super active flux coated cadmium free silver brazing alloy with 35% silver content.
- Special βFast Flowβ flux coating provides twice the base metal cleansing action of conventional silver flux coatings.
- No odors from rubberized compounds yet the flux coating is totally flexible and non-fragile.
- The only flux coated silver flux strong enough to clean oxidized stainless steel.
- Available in any alloy grade or color with small 10# (5kg) minimum orders.
- Available bare as item #3139 for use with 5130 flux.
| All Weld Metal Analysis (Typical Weight %) |
Flux Color: Orange or Custom Colors
| Ag | Cu | Zn |
| 30 | 38 | 32 |
| Typical Mechanical Properties |
Undiluted Weld Metal Maximum Value Up to:
Tensile Strength 45,000 PSI (310 MPa)
Elongation 20%
Conductivity 24.4
Density (Troy oz./cu in.) 4.66
Torch Setting: Slightly carburizing
Temperature Ranges:
| Working Temperature: | Liquidus | Solidus |
| 1255Β°F (679 Β°C) | 1410Β°F (765Β°C) | 1250Β°F (676Β°C) |
| Brazing Instructions |
Welding Techniques: After cleaning metal, preheat generally to 350Β°F (200Β°C) then heat the joint area to 800Β°F (420Β°C). Melt off some flux and allow it to flow throughout the joint. Then add alloy.
Deposition Rates:
| Diameter (mm) | Length (mm) | Weldmetal/Rod | Joint Length/1β³ (25mm) of Rod |
| 1/16 (1.6) | 18β³ (450) | .33 oz (9.2g) | 24β³ (600mm) |
| 3/32 (2.5) | 18β³ (450) | .65 oz (18g) | 44β³ (1100mm) |
| APPROXIMATE ROD PACKAGING & DIMENSIONS |
| Diameter (mm) | 1/16 (1.6) | 3/32 (2.5) |
| Length (mm) | 18β³ (450) | 18β³ (450) |
| Rods / lb | 32 | 16 |
| Rods / kg | 70 | 35 |
| Feet / lb | 48 | 24 |
| Cm / kg | 3150 | 1575 |