| INTERNATIONAL CLASSIFICATIONS |
AWS/ASME A 5.15 EST
ISO 1071: E Fe
DIN 8573: E Fe-1
| FEATURES & APPLICATIONS |
For non-machinable welds on machine bases, furnace grates, exhaust manifolds, etc.
- Nickel free cast iron problem solver, seals in porosity generating contaminants prior to finish welding with nickels.
- Easily clads heat oxidized and oil impregnated castings.
- Perfect color match to cast iron.
- Non-conductive flux coating.
| All Weld Metal Analysis (Typical Weight %) |
Flux Color: Black
| C | Mn | Si | S | P | Fe |
| .12 | .58 | .02 | .03 | .03 | Bal |
| Typical Mechanical Properties |
Undiluted Weld Metal Maximum Value Up to:
Tensile Strength 62,000 PSI (440 MPa)
Yield Strength 50,000 PSI (360 MPa)
Elongation 20%
Hardness Brinell 380, Rockwell C39
| Welding Current & Instructions |
Recommended Current: DC Reverse (+), AC
| Diameter (mm) | 3/32 (2.5) | 1/8(3.25) | 5/32 (4.0) |
| Minimum Amperage | 45 | 70 | 95 |
| Maximum Amperage | 85 | 125 | 150 |
Welding Techniques: Use a stringer or moderate weave technique. When cladding, cover the entire base surface prior to finish welding.
Welding Positions: Flat, vertical up, horizontal, vertical down, overhead
Deposition Rates:
| Diameter (mm) | Length (mm) | Weldmetal/ Electrode | Electrodes per lb (kg) of Weldmetal | Arc Time of Deposition min/lb (kg) | Amperage Setting | Recovery Rate |
| 3/32 (2.5) | 14″(350) | .30 oz (8g) | 53 (117) | 36 (79) | 70 | 100% |
| 1/8 (3.25) | 14″(350) | .62 oz (17g) | 26 (57) | 25 (55) | 100 | 100% |
| 5/32 (4.0) | 14″(350) | 1 oz (28g) | 16 (35) | 20 (44) | 135 | 100% |
| APPROXIMATE ELECTRODE PACKAGING & DIMENSIONS |
| Diameter (mm) | 3/32 (2.5) | 1/8 (3.25) | 5/32 (4.0) |
| Length (mm) | 14″ (350) | 14″ (350) | 14″ (350) |
| Electrodes / lb | 26 | 14 | 10 |
| Electrodes / kg | 57 | 31 | 22 |